@flexo printing tape
Double – Side Tapes
For color printing
Model : 6505 / 5505
Features :
※ Adhesive : Rubber (Solvent
based) adhesive coated on both sides.
※ Carrier : Transparent PVC Film.
※ Liner : 5505 – 110g / m2 PE
coated Draft paper liner, natural color.
6505 – Crepe PVC film liner, brown color.
Semi removable adhesive system for temporary
※ Bonding and repositioning
without leaving residue after removal.
※ During mounting process.
Specifications :
Thickness : 0.1 / 0.2 /0.3 MM
Width : 310 mm and any width
Length : 4.5 / 10 m and any length
Technical data :
※ hickness tolerance : +-0.005
mm
Tack : J Dow No.Close side 10 Open Side 14
※ Peel adhesion : PSTC-3 1.0
kg/25 mm 1.2kg / 25 mm
※ Adhesion Growth : <10% (peel adhesion after
Pressing of 80g/cm2 for 72 hours)
Shear strength : PSTC-7 over 24
hrs with 1 kg
※ Loading on 25 mm x 25 mm, both
sides
Service Temperature : 10-60 degree C
Applications :
※ Temporary mounting of rubber or
photopolymer plates to the printing cylinder or sleeves in flexographic and
letterpress printing
※ Specially designed for mounting
photopolymer plates in printing of business forms, labels, books and newspapers
printing. Etc.
Double-side tapes for printing
|
+zoom
@flexo Tapes
features 100420
No.
|
Thickness
|
Carrier
|
Color
|
Release Liner
|
(mm)
|
(inch)
|
@3505
|
0.10
|
0.004
|
UPVC
|
Clear
|
PE/Kraft Paper
|
@3508
|
0.20
|
0.008
|
UPVC
|
Clear
|
PE/Kraft Paper
|
@3512
|
0.30
|
0.012
|
UPVC
|
Clear
|
PE/Kraft Paper
|
@6505
|
0.10
|
0.005
|
UPVC
|
Clear
|
Crepe PVC
Brown
|
@6508
|
0.20
|
0.008
|
UPVC
|
Clear
|
Crepe PVC
White
|
@6512
|
0.30
|
0.012
|
UPVC
|
Clear
|
Crepe PVC
Green
|
@2248
|
0.18
|
0.007
|
Densified Paper
|
White
|
Glassine Paper
|
@4615
|
0.38
|
0.015
|
Cotton Cloth
|
Beige
|
Glassine Paper
|
@6115
|
0.38
|
0.015
|
Hard compressible foam
|
Off-White
|
White Embossed
PP Liner
|
@6120
|
0.50
|
0.020
|
Hard compressible foam
|
Off-White
|
White Embossed
PP Liner
|
@6115
|
0.38
|
0.015
|
Hard compressible
+ Film
reinforcement
|
Off-White
|
PE / Kraft Paper
|
@6120
|
0.50
|
0.020
|
Hard compressible
+ Film
reinforcement
|
Off-White
|
PE / Kraft Paper
|
@flexo double-side tape for printing
Product No. 6505
Good for Letterpress / Flexo / Vanish and all kinds of printing
Features:
1. Adhesive : Acrylic(Solvent base) adhesive coated on both sides.
2. Carrier : Transparent PVC Film.
3. Liner : Crepe PVC film liner, brown color
4. Semi removable adhesive system for temporary bonding and repositioning without leaving residue after removal.
5. With crepe PVC film liner to avoid air trap during mounting process.
Technical data:
1. Thickness : 0.105 +- 0.005 mm
Close side Open Side
2. Tack : J. Dow No. 12 12
3. Peel Adhesion : PSTC-3 1.0 +- 0.1 kg / 25 mm 1.2 +- 0.1 kg / 25 mm
4. Adhesion Growth : <10 % (Peel adhesion after pressing of 80g /cm 2 for 72 hours)
5. Shear Strength : PSTC-7 Over 24 hrs with 1 kg loading on 25 mm x 25 mm , both sides
6. Service Temperature : 10 ~ 80 degree C
Applications:
1. Temporary mounting of rubber or photopolymer plates to both flat-bed and rotary cylinder for flexo and letterpress printing.
2. Specially designed for mounting photopolymer plates in printing of business forms, labels, books and newspapers printing, etc.
@flexo double-side tape for plate making
Product No. 0497
Good for Letterpress / Flexo washout mounting when plate making.
Features:
1. Adhesive : Acrylic ( solvent based ) adhesive coated on both sides.
2. Carrier : 1/2 mil ( 12 _ ) transparent PET film.
3. Liner : 110g /m 2 PE coated bleached Kraft paper liner.
4. Enhanced carrier - PET film helps clean removal.
5. Moderate adhesion to most substrates.
6. High tack adhesive system that provides quick bonding result.
Technical data:
1. Thickness : 0.09 _ 0.005 mm
2. Tack : J. Dow No. 20
3. Peel Adhesion : PSTC-3 1.2 kg / 25 mm
4. Shear Strength : PSTC-7 Over 24 hrs with 1 kg loading on 25mm x 25mm
5. Service Temperature: -20 ____ __ _ __
6. PH Value : _ 7.0
Applications:
1. Flexo and letterpress mounting on washout board when plate making.
2. Mounting of nameplates, trophies and signs.
3. Bonding of sporting goods - tennis, shoes, leather, etc.
4. Stationery market.
|